垣内 一雄; 天谷 政樹; 宇田川 豊
Annals of Nuclear Energy, 171, p.109004_1 - 109004_9, 2022/06
被引用回数：4 パーセンタイル：76.47(Nuclear Science & Technology)In order to understand the dimensional stability of the fuel rod during long-term use in commercial LWRs, an irradiation growth testing in the Halden reactor of Norway was conducted on various fuel cladding materials including the improved Zr alloy. In this paper, the effect of hydrogen, which was absorbed in the cladding tube due to corrosion, on the irradiation growth behavior was evaluated. Comparison between the specimens with or without pre-charged hydrogen revealed that the effect of hydrogen absorption, accelerating irradiation growth, became significant when the hydrogen content exceeded the hydrogen solubility limit in the corresponding irradiation temperature. Analysis based on this understanding derived growth acceleration effect (0.06
0.01)%/100 ppm, whose denominator is defined as the amount of absorbed hydrogen involved in hydride precipitation under irradiation as a relevant parameter.
天谷 政樹; 垣内 一雄; 三原 武
Proceedings of International Nuclear Fuel Cycle Conference / Light Water Reactor Fuel Performance Conference (Global/Top Fuel 2019) (USB Flash Drive), p.1048 - 1056, 2019/09
New fuel cladding alloys of which composition was changed from conventional ones have been developed by nuclear fuel vendors and utilities. Since the irradiation growth of fuel cladding is one of the most important parameters which determine the dimensional stability of fuel rod and/or fuel assembly during normal operation, the irradiation growth behavior of the improved Zr-based alloys for light-water reactor fuel cladding was investigated. The coupon specimens were prepared from fuel cladding tubes with various kinds of improved Zr-based alloys. The specimens were loaded into test rigs and had been irradiated in the Halden reactor in Norway under several coolant temperature conditions up to a fast-neutron fluence of 
7.8
10
(n/cm
, E 
1 MeV). Irradiation conditions such as specimen temperatures had been continuously monitored during the irradiation. During and after the irradiation, the amount of irradiation growth of each specimen was evaluated as a part of the interim and final inspections. The effect of the difference in alloy composition on the amount of irradiation growth seemed insignificant if the other conditions e.g. the final heat treatment condition at fabrication and the irradiation temperature were the same.